Tổng hợp V2O5 kích thước nanomet bằng phương pháp đốt cháy gel

Lưu Minh Đại, Đào Ngọc Nhiệm, Vũ Thế Ninh, Phạm Ngọc Chức
Author affiliations

Authors

  • Lưu Minh Đại
  • Đào Ngọc Nhiệm
  • Vũ Thế Ninh
  • Phạm Ngọc Chức

DOI:

https://doi.org/10.15625/4566

Abstract

Vanadium pentoxide powder has been synthesised at low temperature (550oC) by the combustion of gel prepared from polyvinyl alcohol (PVA) and vanadium chlorid. The characterization of V2O5 powder is examined by X-ray diffraction (XRD), scanning electron microscopy (SEM) and BET (Brunaure-Emmet-Teller) measurements. Further thermal treatment at 400 - 600oC in 1.5h yields the single phase V2O5 with average size < 50 nm. Its specific surface area is 23.50 m2/g for V2O5.

Downloads

Download data is not yet available.

Downloads

Published

23-08-2014

How to Cite

Đại, L. M., Nhiệm, Đào N., Ninh, V. T., & Chức, P. N. (2014). Tổng hợp V2O5 kích thước nanomet bằng phương pháp đốt cháy gel. Vietnam Journal of Chemistry, 47(2), 198. https://doi.org/10.15625/4566

Issue

Vol. 47 No. 2 (2009)

Section

Articles